Sikafloor®-32 Pronto

• CE Marking and Declaration of Performance to EN 13813:2002 — Screed material and floor screeds — Synthetic resin screed material

• CE Marking and Declaration of Performance to EN 1504-2:2004 — Products and systems for the repair and protection of concrete structures — Part 2: Surface protection systems for concrete — Coating

polyurethane modified polymethyl-methacrylate resin

The Product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +30 °C.
Always refer to packaging.

Refer to the current Safety Data Sheet for information on safe handling and storage.

~100 %

Resistant to many chemicals. Contact Sika technical service for specific information.

IMPORTANT

Exposure to moist or wet heat

Sikafloor® broadcast systems with a minimum thickness of ~3–4 mm, that use this product, can resist short-term moist or wet heat of up to +80 °C, if the exposure is only temporary (less than 1 hour). However, during exposure to moist or wet heat, do not also subject the Sikafloor® broadcast system to chemical and/or mechanical strain, as it may cause damage to the system.

Part A : Part C : Part D = 12.5 : 1 : 25 (by weight)

The amount of Hardener required depends on the substrate temperature:

Note: For ease of handling, units may be split into smaller amounts. Make sure to follow the mixing ratios as described in the Application Information. Always weigh out each part before mixing it.

80 % r.h. max.

Beware of condensation. The substrate and uncured applied product must be at least +3 °C above dew point to reduce the risk of condensation on the surface of the applied product.

No rising moisture (ASTM D4263, polyethylene sheet)

Note: Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity.

Before overcoating the Product, allow:

Note: Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity.

Note: Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity.

~3-4 kg/m² (3-4L/m²) depending on the system applied

Note: Consumption data is theoretical and does not allow for any additional material due to surface porosity, surface profile, variations in level, wastage or any other variations. Apply product to a test area to calculate the exact consumption for the specific substrate conditions and proposed application equipment.

IMPORTANT

Strictly follow installation procedures

Strictly follow installation procedures as defined in Method Statements, application manuals and working instructions which must always be adjusted to the actual site conditions.

APPLICATION EQUIPMENT

• Trowels, including serrated

• Spiked roller

MIXING EQUIPMENT

• Electirc double paddle mixer (>700 W, 300 to 400 rpm)

SUBSTRATE CONDITION

Cementitious substrates (concrete / screed) must be structurally sound and of sufficient compressive strength (minimum 25 MPa) with a minimum tensile strength of 1.5 MPa.

Substrates must be clean, dry and free of all contaminants such as dirt, oil, grease, coatings, laitance, surface treatments and loose friable material.

SELF-SMOOTHING WEARING LAYER MIXING PROCEDURE

1. Mix Part A (resin) for ~30 seconds.
2. Add the required filler.
3. Mix for a further 2 minutes until a uniform mix is achieved.
4. Add Part B (hardener) to Part A.
5. Mix for an additional minute.
6. To ensure thorough mixing, pour materials into another container and mix again to achieve a smooth and uniform mix.
7. During the final mixing stage, scrape down the sides and bottom of the mixing container with a flat or straight edge trowel at least once to ensure complete mixing.

IMPORTANT

Protect from moisture

After application, protect the Product from damp, condensation and direct water contact for at least 1 hour.

IMPORTANT

Ventilation in confined spaces

Always ensure good ventilation when applying the Product in a confined space.

IMPORTANT

No application on rising moisture

Do not apply on substrates with rising moisture.

IMPORTANT

Ventilation for curing

For optimal curing, exchange the air at least seven times per hour. During application and curing, use a forced fresh air supply/exhausting of fumes with appropriate equipment (explosion-proof).

IMPORTANT

Remove foodstuff from application area

Reactive acrylic resins exhibit a characteristic odour during application and before achieving full cure. Once fully cured, they are taint free. All unpackaged goods must be removed from the area of the works during application.

1. Do not apply in the presence of foodstuffs.
2. Isolate any and all foodstuffs, whether packaged or not, from the flooring works during the application process and until the products are fully cured.

IMPORTANT

Pin holes

If the Product is applied on porous substrates during rising temperatures, pin holes may form from rising air.

1. Apply the Product during falling temperatures.

REINFORCED SELF-SMOOTHING WEARING LAYER APPLICATION

1. Pour the mixed Product onto the substrate. Note: The consumption is specified in Application Information.
2. Apply the Product evenly over the surface with a serrated trowel.
3. Back roll the surface in two directions at right angles with a spike roller.
   Note: A seamless finish can be achieved if a "wet" edge is maintained during application.
4. Roll out the reinforcement (Sika® Reemat Premium) onto the wet resin.  Allow a minimum 50 mm overlap on all joints of the reinforcement fleece.
5. Press the reinforcement firmly into the wet resin with a short pile roller.
6. To ensure full saturation of the reinforcement, apply wet on wet an encapsulation layer of the Product with a short pile roller.

Clean all tools and application equipment with Sika® Thinner C immediately after use. Hardened material can only be removed mechanically.