Sikafloor® MultiDur ES-31 ECF
Sikafloor® MultiDur ES-31 ECF is a two part, electrostatic conductive self-smoothing, coloured epoxy flooring system with high chemical resistance. "Total solid epoxy composition acc. to the test method Deutsche Bauchemie e.V. (German Association for construction chemicals)".
- Very high chemical resistance
- High mechanical resistance
- Impervious to liquids
- Abrasion resistant
- Electrostatically conductive
Usage
It is used as:- Chemically highly resistant coating for concrete and screed surfaces in bund areas for the protection against water contaminating liquids (contact Sika technical service for specific information)
- Electrostatic conductive wearing layer for areas subject to chemical and mechanical exposure in production and storage facilities
Advantages
- Very high chemical resistance
- High mechanical resistance
- Impervious to liquids
- Abrasion resistant
- Electrostatically conductive
Colour
Almost unlimited choice of colour shades - available on Indent Only.
Due to the nature of carbon fibres providing the conductivity, it is not possible to achieve exact colour matching. With very bright colours (such as yellow and orange), this effect is increased. Under direct sun light there may be some variations and colour variation, this has no influence on the function and performance of the coating.
Appearance
Self-smoothing system – gloss finish
System Details
APPROVALS / STANDARDS
- Synthetic resin screed material according to EN 13813:2002, Declaration of Performance 02 08 01 02 019 0 000010 201, certified by notified factory production control certification body 0921, certificate of conformity of the factory production control 2017, and provided with the CE marking.
- Coating for surface protection of concrete according to EN 1504-2:2004, Declaration of Performance 02 08 01 02 019 0 000010 201, certified by notified factory production control certification body 0921, certificate of conformity of the factory production control 2017, and provided with the CE marking.
- Reaction to fire classification according to DIN EN 13301-1. Test report No.: 2013-B-1413/01.
- Particle emission certificate Sikafloor®-381 ECF CSM Statement of Qualification - ISO 14644-1, class 4 - Report No. SI 1312-681
- Spark resistance in accordance with UFGS-09 97 23 of coating systems, Test report P 8625-E, Kiwa Polymer Institut
System Structure
Sikafloor® MultiDur ES-31 ECF:
1. Primer + Earthing connection | Sikafloor®-150/-151 + Sika® Earthing Kit |
2. Conductive primer | Sikafloor®-220 W Conductive |
3. Final conductive coating | Sikafloor®-381 ECF filled with Sika® Aggregate-508 |
The system configurations as described must be fully complied with and may not be changed.
Composition
Epoxy
Nominal thickness
~ 1.5 mm
Shore D Hardness
~ 82 (resin filled) | (7 days / +23 °C) |
Abrasion Resistance
~ 40 mg (resin filled) | (CS 10/1000/1000) (8 days / +23 °C) |
Compressive Strength
~ 80 MPa (resin filled) | (14 days / +23 °C) |
Tensile Strength
~ 55 MPa (resin filled) | (14 days / +23 °C) |
Reaction to Fire
Bfl s1 | (EN 13501-1) |
Chemical Resistance
Resistant to many chemicals. Contact Sika technical service for specific information.
Thermal Resistance
Exposure* | Dry heat |
Permanent | +50 °C |
Short-term max. 7 d | +80 °C |
Short-term moist/wet heat* up to +80 °C where exposure is only occasional (i.e. during steam cleaning etc.)
*No simultaneous chemical and mechanical exposure.
USGBC LEED Rating
Conforms to the requirements of LEED EQ Credit 4.2: Low-Emitting Materials: Paints & Coatings SCAQMD Method 304-91 VOC Content <100 g/l.
Electrostatic Behaviour
Resistance to ground1 | Rg < 109 Ω |
Typical average resistance to ground2 | Rg < 106 Ω |
1 In accordance with IEC 61340-5-1 and ANSI/ESD S20.20.
2 Readings may vary, depending on ambient conditions (i.e. temperature, humidity) and measurement equipment.
Application
Ambient Air Temperature
+10 °C min. / +30 °C max.
Relative Air Humidity
80 % r.h. max.
Dew Point
Beware of condensation!
The substrate and uncured floor must be at least 3 °C above dew point to reduce the risk of condensation or blooming on the floor finish.
Substrate Temperature
+10 °C min. / +30 °C max.
Substrate Moisture Content
≤ 4% pbw using Sikafloor®-150.
Test method: Sika®-Tramex meter, CM - measurement or Oven-dry-method.
No rising moisture according to ASTM (Polyethylene-sheet).
Osmosis caused by rising moisture or incorrect primer application is not covered by the product warranty.
Substrates above 4% but less than 6% pbw maybe primed using Sikafloor®-151,
Please note Sikafloor-151 offers no protection against rising moisture.
Waiting Time / Overcoating
Before applying Sikafloor®-220 W Conductive on Sikafloor®-150/151 allow:
Substrate temperature | Minimum | Maximum |
+10 °C | 24 hours | 4 days |
+20 °C | 12 hours | 2 days |
+30 °C | 8 hours | 1 days |
Before applying Sikafloor®-381 ECF on Sikafloor®-220 W Conductive allow:
Substrate temperature | Minimum | Maximum |
+10 °C | 26 hours | 7 days |
+20 °C | 17 hours | 5 days |
+30 °C | 12 hours | 4 days |
Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
Applied Product Ready for Use
Temperature | Foot traffic | Light traffic | Full cure |
+10 °C | ~ 24 hours | ~ 3 days | ~ 10 days |
+20 °C | ~ 18 hours | ~ 2 days | ~ 7 days |
+30 °C | ~ 12 hours | ~ 1 days | ~ 5 days |
Note: Times are approximate and will be affected by changing ambient conditions
Consumption
Coating | Product | Consumption |
Primer | Sikafloor®-150/-151 | 1-2 x ~ 0.3 - 0.5 kg/m² |
Levelling (if required) | Sikafloor®-150/-151 levelling mortar | Refer to PDS of Sikafloor®-150/151 |
Earthing connection | Sika® Earthing Kit | 1 earthing point per approx. 200 -300 m², min. 2 per room. |
Conductive primer | Sikafloor®-220 W Conductive | 1 x 0.08 - 0.10 kg/m² |
Final conductive coating | Sikafloor®-381 ECF filled with Sika® Aggregate-508* | 2.5 kg/m² Binder + quartz sand |
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc.
*Other quartz sand type will have an effect on the product, such as filling grade, levelling properties and aesthetics. Generally, the lower the temperature the less the filling grade.