Sikafloor®-262 AS N

• Environmental Product Declaration (EPD) in accordance with EN 15804. EPD independently verified by Institut für Bauen und Umwelt e.V. (IBU)

• Conforms with LEED v4 EQ credit: Low-emitting materials

• Conforms with LEED v4 MR credit: Building product disclosure and optimization — Environmental Product Declarations (option 1)

• CE marking and declaration of performance based on EN 13813:2002 Screed material and floor screeds — Screed material — Properties and requirements — Synthetic resin screed material

• CE marking and declaration of performance based on EN 1504-2:2004 Products and systems for the protection and repair of concrete structures — Surface protection systems for concrete — Coating

• Fire testing EN 13501-1, Sikafloor®-262 AS N, MPA, Report No. 2007-B-0181/17

• Coating Compatibility AA-P 128, Sikafloor®, Polymer Institut, Report No. P 5541

• Material testing PV 3.10.7, Sikafloor®-262 AS N, HQM, Report No. 14-04-14201871-

• Particle Test ISO 14644-1, Sikafloor®-262 AS N, CSM Fraunhofer, Certificate No.

• Outgassing emissions VDI 2083-17, Sikafloor®-262 AS N, CSM Fraunhofer, Certifica

• Biological Resistance ISO 846, Sikafloor®-262 AS N, No. SI 1412-740

Epoxy

12 months from date of production

The Product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +30 °C. Always refer to packaging.

Refer to the current Safety Data Sheet for information on safe handling and storage.

~97 %

~97 %

This product fulfils the requirements of ATEX 153.

Readings may vary, depending on ambient conditions (i.e. temperature, humidity) and measurement equipment.

IMPORTANT

No simultaneous mechanical and chemical strain

While the product is exposed to temperatures up to +60 °C, do not also subject it to chemical and/or mechanical strain, as it may cause damage to the product.

Laboratory defined resistance to many individual chemicals. Before proceeding, contact Sika Technical Services for specific information.

80 % r.h. max

Beware of condensation. The substrate and uncured applied product must be at least +3 °C above dew point to reduce the risk of condensation or blooming on the surface of the applied product. Low temperatures and high humidity conditions increase the probability of blooming.

≤ 4% pbw using Sikafloor®-150.

Test method: Sika®-Tramex meter, CM - measurement or Oven-dry-method.

No rising moisture according to ASTM (Polyethylene-sheet).

Osmosis caused by rising moisture or incorrect primer application is not covered by the product warranty.

Substrates above 4% but less than 6% pbw maybe primed using Sikafloor®-151,

Please note Sikafloor-151 offers no protection against rising moisture.

IMPORTANT

Temporary moisture barrier

If the substrate moisture content measured above the figures listed above, apply a temporary moisture barrier consisting of Sikafloor® EpoCem®.

1. Contact Sika technical services for more information.

Note: Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity.

Note: Consumption data is theoretical and does not allow for any additional material due to surface porosity, surface profile, variations in level, wastage or any other variations. Apply product to a test area to calculate the exact consumption for the specific substrate conditions and proposed application equipment.

Excessive layer thickness

Note: Applying the Product in excess of the stated thickness causes reduced conductivity.

Select the most appropriate equipment required for the project:

MIXING

• Electric single paddle mixer (300-400 rpm)

• Electric double paddle mixer (> 700 W, 300-400 rpm)

• Scraper

• Clean mixing containers

APPLICATION

• Mixed material carrier

• Notched trowel or pin rake

• Steel spike rollers

IMPORTANT

Incorrect treatment of cracks

The incorrect assessment and treatment of cracks may lead to a reduced service life and reflective cracking.

TREATMENT OF JOINTS AND CRACKS

Construction joints and existing static surface cracks in substrate require pre-treating before full layer application. Use Sikadur® or Sikafloor® resins.

SUBSTRATE CONDITION

Cementitious substrates (concrete / screed) must be structurally sound and of sufficient compressive strength (minimum 25 MPa) with a minimum tensile strength of 1.5 MPa.

Substrates must be clean, dry and free of all contaminants such as dirt, oil, grease, coatings, laitance, surface treatments and loose friable material.

1. Mix Part A (resin) for ~10 seconds with a single paddle mixer (300–400 rpm).
2. Add Part B (hardener) to Part A. Switch to an electric double paddle mixer (300–400 rpm, > 700 W).
3. While mixing Parts A + B, gradually add the required filler or aggregates.Note: Avoid over mixing to minimise air entrainment.
4. Mix for a further 2 minutes until a uniform mix is achieved.
5. To ensure thorough mixing pour materials into a clean container and mix again for at least 1 minute to achieve a smooth consistent mix.
6. During the final mixing stage, scrape down the sides and bottom of the mixing container with a straight edge trowel or spatula.

IMPORTANT

Temporary heating

If temporary heating is required, do not use gas, oil, paraffin or other fossil fuel heaters, these produce large quantities of both CO₂ and H₂O water vapour, which may adversely affect the finish. For heating use only electric powered warm air blower systems.

IMPORTANT

Performing pre-trials

Pre-trials/mock-up applications must be performed and procedures agreed with all parties before full project application.

IMPORTANT

Indentations

Under certain conditions, underfloor heating or high ambient temperatures combined with high point loading may lead to indentations in the resin.

IMPORTANT

Protect from moisture

After application, protect the Product from damp,

condensation and direct water contact for at least 24 hours.

Preconditions

IMPORTANT Do not blind the primer.The conductive priming coat has been applied and has dried tack-free all over.

1. Pour the mixed Product onto the surface. Note: The consumption is specified in Application Information.
2. Apply the Product evenly over the surface with a serrated trowel.
3. Turn the serrated trowel and smooth the surface for an aesthetically higher grade of finish.
4. IMPORTANT This process must happen within 10 minutes of application. Back roll the surface in two directions at right angles with a spike roller.

IMPORTANT

Temporary moisture barrier

≤ 4% pbw using Sikafloor®-150

Test method: Sika®-Tramex meter, CM - measurement or Oven-dry-method.

No rising moisture according to ASTM (Polyethylene-sheet).

Osmosis caused by rising moisture or incorrect primer application is not

covered by the product warranty.

Substrates above 4% but less than 6% pbw maybe primed using Sikafloor®-151,

Please note Sikafloor-151 offers no protection against rising moisture

.

IMPORTANT

Temporary moisture barrier

If the substrate moisture content measured above the figures listed above, apply a temporary moisture barrier consisting of Sikafloor® EpoCem®. 1. Contact Sika technical services for more information.

Clean all tools and application equipment with Sika® Thinner C immediately after use. Hardened material can only be removed mechanically.