Sikafloor®-264 T AU
High Build Durable 100% Solids Pigmented Non Blooming Epoxy Coating
SikafloorSikafloor®-264 T AU is a thixotropic, textured 2- componant solvent free pigmented 100% solids high build epoxy coating for durable, decorative finishes. It can be appied to vertical surfaces in addition to providing a durable floor surface.
- Tough / Durable
- Good abrasion resistance
- Excellent resistance to whitening / blooming from early exposure to surface moisture
- Can be applied on vertical and horizontal surfaces
- Easily cleaned and maintained
- Very good chemical resistance (Refer to Sika Chemical resistance data)
Usage
SikafloorSikafloor®-264 T AU can be used in a variety of Industrial and commercial applications;- Clean rooms - laboratories
- Pharamaceutical
- Food related premises
- Correctional facilities
- Automotive workshops
- Stadiums
- Amenities/washrooms
- General accessways
Advantages
- Tough / Durable
- Good abrasion resistance
- Excellent resistance to whitening / blooming from early exposure to surface moisture
- Can be applied on vertical and horizontal surfaces
- Easily cleaned and maintained
- Very good chemical resistance (Refer to Sika Chemical resistance data)
Packaging
9.7kg kit (7.3L): Part A + Pigment 7.7 kg, Part B 2 kg
Colour
Resin - Part A Beige colour liquid before being pigmented.
Hardener - Part B Transparent liquid
Colours: Sikafloor®-264 T AU system is available in a range of standard RAL colours
- Non standard colours can be supplied on request.
- Refer to the Sikafloor epoxy colour chart for details
Product Details
Shelf Life
Twelve (12) months from date of manufacture when stored as stated.
Storage Conditions
Store away from direct sunlight and idealy between +5 to 35 degrees C
Density
Mixed product: 1.33 kg/litre (at +23°C)
Volatile organic compound (VOC) content
Conforms to Aust.Standard test ASTM D3960.
Greenstar Building Council of Australia - Green Star Office Design V2 IEQ-13 / Green Star Office Interiors V1.1 IEQ-11
Shore D Hardness
76 (7 days / +23 degrees C)
Abrasion Resistance
70mg (CS10/1000/1000) (8 days / +23 Degrees C) DIN. 53 109 Taber Abrader test
Chemical Resistance
Sikafloor®-264 T AU has ecellent resistance to a wide range of chemicals. Refer to Sika Technical for specific information on resistance to chemicals.
Gloss Level
Low sheen to Semi gloss (depending on temperature at application)
Application
Layer Thickness
Approx total system DFT 0.6- 0.7mm (Depending on substrate density and profile)
Ambient Air Temperature
+10 degrees C min. / +30 degrees C max.
Relative Air Humidity
80% r.h max.
Dew Point
Beware of condensation The subsrate and uncured floor must be at least 3 degrees C above dew point to reduce the risk of condensation or blooming of the surface finish.
Substrate Temperature
+10 degrees C min. / +30 degrees C min.
Pot Life
Approx values +10 degrees C approx 25 min. +20 degrees C 15 min. +30 degrees C 8 min
Waiting Time / Overcoating
Intercoat times beween system layers
Substrate Temperature Minimum Maximum
+10 degrees C 24 hours 4 days
+20 degrees C 12 hours 2 days
+30 degrees C 6 hours 1 day
Applied Product Ready for Use
Temperature Foot trafffic Light Traffic Full cure
+10 degrees C 72 hours 6 days 10 days
+20 degrees C 24 hours 4 days 7 days
+30 degrees C 18 hours 2 days 5 days
Note: These are approximates and will be affected by changing ambient conditions
APPLICATION INSTRUCTIONS
Prior to application, confrim the substrate moisture content, rh and dew point. If> 4% above pbw Sikafloor EpoCem Moisture barrier system may be applied prior to installation of the Sikafloor®-264 T AUsystem.
MIXING
Add the Part B into Part A and mix the full kit for a minimum of 2 minutes. Sikafloor®-264 T AU must be thorougly mixed using a low speed stirrer (300 - 400 rpm)
APPLICATION
Placing the kits at an even rate of pot life and joining up wet edges progressively within even time frames is critical for optimum results. If this is not adhered to then differing colour shades will result when the product has reached touch dry stage. Application: Apply product using a medium to long knap roller (15-20mm) with a central pole double frame arrangement. Apply evenly at the prescribed coverage rate then "lay off " in the oppoosite direction of rolling for optimum results. Final layoff technique - take the weight of the roller and lift the roller from the surface when completing to lay off stroke. Not adopting the technique and/or not having suffient manpower to execute this proceedure will likely result in uneven appearance.
CLEANING OF TOOLS
Clean all tools immediately after use Sika Thinner C. Hardened and/or cured material can only be removed mechanically.
CLEANING
Sikafloor®-264 T AU should be kept as clean as possible to maximise durability and reduce abrasion. Good housekeeping practices should be followed when Chemical spills occur. Clean with neutral based, non solvent based cleaning chemicals. - Refer to Sikafloor Cleaning Guidelines document for more details.