Sikafloor® MultiDur EB-31
Slip resistant unicolour epoxy flooring system with very good chemical and mechanical resistance
Sikafloor® MultiDur EB-31 is a slip resistant, coloured epoxy flooring system with very good chemical and mechanical resistance.
- Good resistance to abrasion
- Very good resistance to specific chemicals
- Very good mechanical resistance
- Impermeable to liquids
Usage
The System is used in industrial buildings such as:- Automotive facilities
- Chemical and processing facilities
- Food and beverage facilities
- The System may only be used by experienced professionals.
- The System may only be used for interior applications.
Advantages
- Good resistance to abrasion
- Very good resistance to specific chemicals
- Very good mechanical resistance
- Impermeable to liquids
Colour
Cured system colour | Available in various colour shades. |
Appearance
Slip resistant, gloss finish
System Details
APPROVALS / STANDARDS
Slip resistance test report DIN 51130, Roxeler, No. 020023-19-31
System Structure
Layer | Product |
Primer | Sikafloor®-150 Sikafloor®-151 |
Wearing layer | Sikafloor®-381 |
Broadcast in excess | Silicon carbide (0.5–1.0 mm) or Quartz sand (0.6-1.2 mm) Or Sika Aggregate-501 |
Top coat | Sikafloor®-381 + 5 % Sika® Thinner C |
Composition
Epoxy
Nominal thickness
2 mm to 3 mm
Tensile Adhesion Strength
≥ 1.5 MPa | (EN 1542) |
Reaction to Fire
Class Bfl-s1 | (EN 13501-1) |
Chemical Resistance
Sikafloor®-381 provides the chemical resistance. Refer to Product Data Sheet.
Note: The exposed aggregates can be affected through various chemicals. A surface finish of an acrylic dispersion as a protection and maintenance layer is recommended.
Skid / Slip Resistance
R 12; V 6 | (DIN 51130) |
Application
Ambient Air Temperature
Maximum | +30 °C |
Minimum | +10 °C |
Relative Air Humidity
Maximum | 80 % r.h. max. |
Dew Point
Beware of condensation!
The substrate and uncured floor must be at least 3 °C above dew point to
reduce the risk of condensation or blooming on the floor finish.
Substrate Temperature
Maximum | +30 °C |
Minimum | +10 °C |
Substrate Moisture Content
≤ 4% pbw using Sikafloor®-150
≤ 6% pbw using Sikafloor®-151
Test method: Sika®-Tramex meter, CM - measurement or Oven-dry-method.
No rising moisture according to ASTM (Polyethylene-sheet).
Osmosis caused by rising moisture or incorrect primer application is not
covered by the product warranty.
Waiting Time / Overcoating
Before applying Sikafloor®-381 on Sikafloor®-150/ -151 allow:
Temperature | Minimum | Maximum |
+10 °C | ~24 hours | ~4 days |
+20 °C | ~12 hours | ~48 hours |
+30 °C | ~8 hours | ~24 hours |
Before applying Sikafloor®-381 on Sikafloor®-381 allow:
Temperature | Minimum | Maximum |
+10 °C | ~24 hours | ~48 hours |
+20 °C | ~18 hours | ~24 hours |
+30 °C | ~6 hours | ~12 hours |
Note: Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity.
Applied Product Ready for Use
Temperature | Foot traffic | Light traffic | Full cure |
+10 °C | ~24 hours | ~3 days | ~10 days |
+20 °C | ~18 hours | ~2 days | ~7 days |
+30 °C | ~12 hours | ~24 hours | ~5 days |
Note: Times apply when the last layer of the system has been applied. Times are affected by changing ambient conditions, particularly temperature and relative humidity.
Consumption
Layer | Product | Consumption |
Primer | Sikafloor®-150 or Sikafloor®-151 or | 1–2 × ~0.3 kg/m² to 0.5 kg/m² |
Wearing layer | Sikafloor®-381 unfilled | ~1.6 kg/m² |
Broadcast in excess | Silicon carbide (0.5–1.0 mm) or Quartz sand (0.6-1.2 mm) Or Sika Aggregate-501 | ~4-6 kg/m² |
Top coat | Sikafloor®-381 + 5 % Sika® Thinner C | 1 × ~0.75 kg/m² to 0.85 kg/m² |
Note: Consumption data is theoretical and does not allow for any additional material due to surface porosity, surface profile, variations in level, wastage or any other variations. Apply product to a test area to calculate the exact consumption for the specific substrate conditions and proposed application equipment.