SikaTack® MOVE Transportation
All-in-one solution for Bus, Coach and Truck Glass Replacement
SikaTack® MOVE Transportation is a cold-applied adhesive specially designed for glass replacement and gap filling application for buses, coaches and trucks. It provides a good weathering stability and is therefore suitable for open joints.
- Short Drive Away Time for commercial vehicles
- Suitable for bonding and gap filling
- Exhibits good weathering stability
- Compatible with Black-Primerless and All Black installation processes
- Solvent-free
- Ideal product for glass replacement on commercial vehicles
PRODUCT BENEFITS
- Short Drive Away Time for commercial vehicles
- Suitable for bonding and gap filling
- Exhibits good weathering stability
- Compatible with Black-Primerless and All Black installation processes
- Solvent-free
- Ideal product for glass replacement on commercial vehicles
Usage
SikaTack® MOVE Transportation has been specially designed as an all-in-one solution for the windshield replacement of commercial vehicles such as buses and trucks. Thanks to its weathering stability it can be used for both bonding and gap filling. It is ideal for mobile and in-house installations.SikaTack® MOVE Transportation is suitable for experienced users only.
This product and related process information is designed for vehicle Glass Replacement. For other applications, tests with actual substrates and conditions have to be performed to ensure adhesion and material compatibility.
Packaging
| Unipack | 600 ml |
Product Details
| Chemical base | 1-component polyurethane | |
| Color (CQP001-1) | Black | |
| Cure mechanism | Moisture-curing | |
| Density (uncured) | 1.2 kg/l | |
| Non-sag properties (CQP061-1) | Very good | |
| Application temperature | product ambient | 5 ─ 35 °C 5 ─ 35 °C |
| Skin time (CQP019-1) | 20 minutes A | |
| Open time (CQP526-1) | 15 minutes A | |
| Curing speed (CQP049-1) | See diagram 1 | |
| Shore A hardness (CQP023-1 / ISO 48-4) | 65 | |
| Tensile strength (CQP036-1 / ISO 527) | 8 MPa | |
| Elongation at break (CQP036-1 / ISO 527) | 300 % | |
| Tear propagation resistance (CQP045-1 / ISO 34) | 10 N/mm | |
| Tensile lap-shear strength (CQP046-1 / ISO 4587) | 5 MPa | |
| Minimum Drive Away Time for supported glass | < 40 kg < 75 kg | 2 hours B/C 4 hours B/C |
| Service temperature (CQP509-1 / CQP513-1) | -40 ─ 90 °C | |
| Shelf life | 12 months D |
| CQP = Corporate Quality Procedure | A) 23 °C / 50 % r. h. | B) Details about MDAT contact Sika |
| C) 5 °C / 80 % r. h. ─ 40 °C / 20 % r. h. | D) storage below 25 °C |
CURE MECHANISM
SikaTack® MOVE Transportation cures by reaction with atmospheric moisture. At low temperatures the water content of the air is generally lower and the curing reaction proceeds more slowly (see diagram 1).
Diagram 1: Curing speed of SikaTack® MOVE Transportation
CHEMICAL RESISTANCE
SikaTack® MOVE Transportation is generally resistant to fresh water, seawater, diluted acids and diluted caustic solutions; temporarily resistant to fuels, mineral oils, vegetable and animal fats and oils; not resistant to organic acids, glycolic alcohol, concentrated mineral acids and caustic solutions or solvents.
Application
Surface preparation
Surfaces must be clean, dry and free from grease, oil, dust and contaminants.
The bond faces must be treated according to Sika's Black-Primerless or All Black installation process. Further information on the application and use of Pre-treatments can be found in the corresponding Product Data Sheet.
Glass without ceramic coatings need proper UV protection.
Application
It is recommended to apply SikaTack® MOVE Transportation with a powerful battery operated application gun.
Consider that the viscosity will increase at low temperature. For easy application, condition the adhesive at ambient temperature prior to use.
To ensure a uniform thickness of the bondline it is recommended to apply the adhesive in the form of a triangular bead (see figure 1).
Figure 1: Compressing adhesive bead to final size
The open time is significantly shorter in hot and humid climates. The glass must always be installed within the open time. Never install a glass after the product has built a skin.
Removal
Uncured SikaTack® MOVE Transportation can be removed from tools and equipment with Sika® Remover-208 or another suitable solvent. Once cured, the material can only be removed mechanically. Hands and exposed skin have to be washed immediately using a suitable industrial hand cleaner and water. Do not use solvents on skin.